PVC Rigid Sheet is a kind of high-tech and environment-friendly product, produced by
advanced equipment imported from Austria. It is extruded and shaped by PVC powder, which is
the main ingredient, and mixed with other additives, such as stabilizer. PVC Rigid sheet has
many advantages, such as strong, hard, shinny or matt surface, UV resistance,
anti-corrosion, etc.. It is perfect substitute of stainless steel and other
anti-corrodibility composite materials. It is widely used in many fields: chemical industry,
oil industry, galvanization, environment-protecting equipment, mining industry, medical
appliance, advertising, construction and so on.
Products Details
Description
|
PVC Rigid Board/sheet/Panel; PVC Board/sheet/Panel
|
Width(mm)
|
910, 1000, 1220, 1300, 1500 etc. max. width is 1500mm
|
Length(mm)
|
1830, 2000, 2440, 3000 etc. Upon your request
|
Thickness(mm)
|
1-30mm
|
Density
|
1.4~1.6g/cm3 --- grade A+ :1.4g/cm3; grade A: 1.5g/cm3; grade B: 1.6g/cm3
|
Surface
|
Glossy, matt, textured available upon your design
|
Colors
|
white, light grey, dark grey, yellow available upon your request
|
Application
-
Industry: chemical industry, galvanizing industry.
-
Advertising: display board, printable screen printing, digital printing, laminated.
-
Construction material: indoor decorating, wall paneling, composite door panel.
-
Electron: electric and communication equipments.
Specical Application
-
UV Stabilized Sheet in 3 years, 5 years, 10 years used for outside advertising and
constructions, such as Signboard, wall claddings, air vents and so on.
-
Color Stabilized sheet in 1 year, 3 years, 5 years used for inside or outside where
there are high request about color, such as lettering, display for long time and so
on.
Tolerances
RANGE (based on thickness)
|
THICKNESS(mm)
|
LENGTH(mm)
|
WIDTH(mm)
|
RECTANGULARITY
|
< 3mm
|
±(0.08+0.03*d)
|
within ±10mm
|
within ±5mm
|
within +3mm/m
|
≥3mm
|
Mechanical Features
PROPERTY
|
TEST METHOD (ASTM D)
|
CONDITION
|
VALUE(Based on 15mm)
|
UNIT
|
Tensile Strength at Yield
|
ASTM D 638
|
Specimen: Type I Speed: 10mm/min
|
10MPa
|
1,450psi
|
Elongation at Break
|
Specimen: Type I Speed: 10mm/min
|
5
|
%
|
Tensile Modulus
|
Specimen: Type V Speed: 1mm/min
|
700
|
Mpa
|
Flexural Strength
|
ASTM D 790
|
127mm×12.91mm×3.77mm Speed: 1.6mm/min Span: 59mm
|
12.6MPa
|
18,270psi
|
Flexural Modulus
|
460MPa
|
66,700psi
|
Impact Strenght
|
ASTM D6110-06
|
With:6.65mm;Depth:12.86mm Heating rate:120℃/h Load:0.455Mpa
|
15
|
J/m
|
Dielectric Strength
|
ASTM D 149
|
|
10
|
kv/mm
|
Physical Features
PROPERTY
|
TEST METHOD (ASTM D)
|
CONDITION
|
VALUE(Based on 15mm)
|
UNIT
|
Specific Gravity
|
ASTM D 792
|
|
0.6
|
g/cm3
|
Water Absorption
|
ASTM D 570
|
76.2mm×25.4mm Drying: 50℃,24hrs; Immersion: 25℃,24hrs
|
0.37
|
%
|
Shore D Hardness
|
ASTM D 2240
|
Type D
|
63
|
D
|
Thermal Features
PROPERTY
|
TEST METHOD (ASTM D)
|
CONDITION
|
VALUE(Based on 6mm)
|
UNIT
|
Heat Deflection Temperature
|
ASTM D648-07 Method B
|
Width:6.65mm; Depth:13.07mm Heating rate:120℃/h; Load:1.82MPa
|
61.4
|
℃
|
Width:6.65mm; Depth:12.86mm Heating rate:120℃/h; Load:0.455MPa
|
70.9
|
℃
|
Heat Distortion Temperature (under load at 264 psi)
|
ASTM D 648
|
|
120
|
℃
|
Coefficient of linear Expansion
|
ASTM D 696
|
|
2.9×10ˉ5
|
in/in/°F
|
Thermal Conductivity
|
ASTM D 177
|
|
0.06
|
W/m°K
|
Packing
PE bags package for 1220*2440mm
|
Wood pallets package for 900*1500mm
|